General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.42 % Show Material materials with Absorción de agua of 0.42 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.49 g/cm³ Show Material materials with Densidad of 1.49 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Material materials with Elongación of 2 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 31 J/m Show Material materials with Impact strength, Izod notched, ASTM of 31 J/m | ASTM D 256 |
23.0 °C | 30 J/m Show Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 4.71 GPa Show Material materials with Módulo de flexión of 4.71 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 5.88 GPa Show Material materials with Módulo elástico of 5.88 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 56 MPa Show Material materials with Resistencia a la tracción of 56 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A |
23.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.29E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 5.29E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 200 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 200 °C | ASTM D 648 | 0.45 MPa, 6.4 mm, unannealed | |
Temperatura de reblandecimiento Vicat | 180 °C Show Material materials with Temperatura de reblandecimiento Vicat of 180 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.04 - 1.06 % Show Material materials with Contracción of 1.04 - 1.06 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1.15 - 1.18 % Show Material materials with Contracción transversal of 1.15 - 1.18 % | SABIC method |
Velocidad de flujo de la masa derretida | 36 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 36 g/10min | ASTM D 1238 | |
Velocidad de flujo del volumen derretido | 52 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 52 cm³/10min | ISO 1133 | 265°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover,Food Processor,Forward Lighting,Motorcycle,Non-LED Lighting,Personal Care,Rear/Signal Lighting,Scooter/Moped | |
Fillers | Mineral Powder | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm |