Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.13 % Show Material materials with Absorción de agua of 0.13 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.25 g/cm³ Show Material materials with Densidad of 1.25 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 65 MPa Show Material materials with Límite elástico of 65 MPa | ISO 527 | 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.35 GPa Show Material materials with Módulo de flexión of 2.35 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.35 GPa Show Material materials with Módulo elástico of 2.35 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 70 MPa Show Material materials with Resistencia a la tracción of 70 MPa | ISO 527 | 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 11 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 135 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 135 °C | ISO 75/Ae | 1.8 MPa | |||
Temperatura de reblandecimiento Vicat | 156 °C Show Material materials with Temperatura de reblandecimiento Vicat of 156 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.7 [-] Show Material materials with Constante dieléctrica of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Óptico
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.6 % Show Material materials with Contracción of 0.4 - 0.6 % | SABIC method |
Velocidad de flujo del volumen derretido | 5 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min | ISO 1133 | 300°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building/Construction Sheet,Enclosures,LED Lighting,Non-LED Lighting,Rail Cabin Interiors | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Barrel - Zone 1 Temperature: 260-300°C, Barrel - Zone 2 Temperature: 260-290°C, Barrel - Zone 3 Temperature: 260-290°C, Hopper Temperature: 100-120°C, Adapter Temperature: 240-280°C, Die Temperature: 240-300°C, Melt Temperature: 260-300°C | |