| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.16 % Show Material materials with Absorción de agua of 0.16 % | ASTM D 570 | 24 Hours |
Absorción de agua, equilibrio | 23.0 °C | 0.32 % Show Material materials with Absorción de agua, equilibrio of 0.32 % | ASTM D 570 |
Densidad | 23.0 °C | 1.25 g/cm³ Show Material materials with Densidad of 1.25 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 4.8 % Show Material materials with Elongación of 4.8 % | ASTM D 638 | 6.35 mm |
Flexural yield strength | 23.0 °C | 89 MPa Show Material materials with Flexural yield strength of 89 MPa | ASTM D 790 | 6.4 mm |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 854 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 854 J/m | ASTM D 4812 |
Límite elástico | 23.0 °C | 52 MPa Show Material materials with Límite elástico of 52 MPa | ASTM D 638 | 6.35 mm |
Módulo de flexión | 23.0 °C | 3.51 GPa Show Material materials with Módulo de flexión of 3.51 GPa | ASTM D 790 | 6.4 mm |
Módulo elástico | 23.0 °C | 3.17 GPa Show Material materials with Módulo elástico of 3.17 GPa | ASTM D 638 | 6.4 mm |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 1189 J/(kg·K) Show Material materials with Calor específico of 1189 J/(kg·K) | ASTM C 351 | ||
Coeficiente de dilatación térmica | 23.0 °C | 3.24E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 3.24E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Conductividad térmica | 23.0 °C | 0.13 W/(m·K) Show Material materials with Conductividad térmica of 0.13 W/(m·K) | ASTM C177 | ||
Heat deflection temperature, 0.45 MPa | 133 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 133 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating | 2.99mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.4 [-] Show Material materials with Constante dieléctrica of 2.4 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 6.5E-3 [-] Show Material materials with Factor de disipación of 6.5E-3 [-] | ASTM D 150 | at 1 MHz |
Resistividad eléctrica | 23.0 °C | 2.40E+15 Ω·m Show Material materials with Resistividad eléctrica of 2.40E+15 Ω·m | ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.6 % Show Material materials with Contracción of 0.4 - 0.6 % | SABIC method | 6.4 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Transfer,Lab Ware and Clinical Diagnostics,Medical Device,Monitoring and Imaging,Renal and Blood Handling | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Time (Blowing Agent): 4hrs, Drying Temperature (Blowing Agent): 105°C, Drying Temperature (Resin): 120°C, Drying Time (Resin): 3-4hrs, Drying Time (Resin, Cumulative): 48hrs, Melt Temperature: 290-315°C, Nozzle Temperature: 270-295°C, Middle Temperature: 295-310°C, Rear Temperature: 255-265°C, Mold Temperature: 70-95°C | |