Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.06 g/cm³ Show Material materials with Densidad of 1.06 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 8 % Show Material materials with Elongación of 8 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 74 MPa Show Material materials with Flexural yield strength of 74 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 98 MPa Show Material materials with Hardness, Ball Indentation of 98 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 114 [-] Show Material materials with Hardness, Rockwell R of 114 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ISO 527 | 50 mm/min |
Módulo de flexión | 23.0 °C | 2.5 GPa Show Material materials with Módulo de flexión of 2.5 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.5 GPa Show Material materials with Módulo elástico of 2.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la tracción | 23.0 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | ISO 527 | 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75/Ae | 1.8 MPa | |||
Temperatura de reblandecimiento Vicat | 102 °C Show Material materials with Temperatura de reblandecimiento Vicat of 102 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.7 [-] Show Material materials with Constante dieléctrica of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 9E-3 [-] Show Material materials with Factor de disipación of 9E-3 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 18 kV/mm Show Material materials with Rigidez dieléctrica of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo de la masa derretida | 25 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 25 g/10min | ISO 1133 | 220°C/10.0 kg | |
Velocidad de flujo del volumen derretido | 24 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 24 cm³/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Coffee Maker/Espresso Machine,Data Management,Electronic Components,Food Transportation,Gas/Electric Oven,Heavy Vehicles,Lawn/Garden,Power Manangement,Refrigerator,Security/Detection,Swimming Pool/Spa,Wiring Devices | |
| Processing methods | Drying Temperature: 85-95°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 210-250°C, Front - Zone 3 Temperature: 220-260°C, Middle - Zone 2 Temperature: 220-260°C, Rear - Zone 1 Temperature: 200-240°C, Hopper Temperature: 60-80°C, Mold Temperature: 40-80°C | |