Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.4 % Show Material materials with Elongación of 2.4 % | ASTM D 638 | Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 97 J/m Show Material materials with Impact strength, Izod notched, ASTM of 97 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 610 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 610 J/m | ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut |
Módulo de flexión | 23.0 °C | 8.9 GPa Show Material materials with Módulo de flexión of 8.9 GPa | ISO 178 | 2 mm/min, 64mm |
Módulo elástico | 23.0 °C | 7.61 GPa Show Material materials with Módulo elástico of 7.61 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 120 MPa Show Material materials with Resistencia a la tracción of 120 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | -30.0 °C | 1.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-5 1/K | ISO 11359-2 |
Coeficiente de dilatación térmica transversal | -30.0 °C | 1.55E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.55E-4 1/K | ISO 11359-2 |
Heat deflection temperature, 1.80 MPa | 153 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 153 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Temperatura de reblandecimiento Vicat | 164 °C Show Material materials with Temperatura de reblandecimiento Vicat of 164 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 % Show Material materials with Contracción of 0.4 % | SABIC method | 48 hrs @ 23°C |
Contracción transversal | 23.0 °C | 0.8 % Show Material materials with Contracción transversal of 0.8 % | SABIC method | 48 hrs @ 23°C |
Velocidad de flujo de la masa derretida | 11 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 11 g/10min | ISO 1133 | 230°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | It is used in automotive exterior applications. | |
| Fillers | 20% Glass Fiber | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |