General
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 67 % Show Material materials with Elongación of 67 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 5.5 % Show Material materials with Elongation at yield of 5.5 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 130 MPa Show Material materials with Hardness, Ball Indentation of 130 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 63 MPa Show Material materials with Límite elástico of 63 MPa | ISO 527 | 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.35 GPa Show Material materials with Módulo elástico of 2.35 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 50 MPa Show Material materials with Resistencia a la tracción of 50 MPa | ISO 527 | 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | ||
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 40 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C |
Heat deflection temperature, 1.80 MPa | 121 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 121 °C | ISO 75/Ae | 1.8 MPa | |
Temperatura de reblandecimiento Vicat | 138 °C Show Material materials with Temperatura de reblandecimiento Vicat of 138 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo del volumen derretido | 40 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 40 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | LED Lighting | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C |