General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.09 % Show Material materials with Absorción de agua of 0.09 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.18 g/cm³ Show Material materials with Densidad of 1.18 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 108 % Show Material materials with Elongación of 108 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 55 J/m Show Material materials with Impact strength, Izod notched, ASTM of 55 J/m | ASTM D 256 | ||
23.0 °C | 687 J/m Show Material materials with Impact strength, Izod notched, ASTM of 687 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 63 MPa Show Material materials with Límite elástico of 63 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.41 GPa Show Material materials with Módulo elástico of 2.41 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 58 MPa Show Material materials with Resistencia a la tracción of 58 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 65 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 65 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 5 kJ/m² | ISO 179/2C | ||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 60 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 125 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Temperatura de reblandecimiento Vicat | 140 °C Show Material materials with Temperatura de reblandecimiento Vicat of 140 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Compliant, 94V-2 Flame Class Rating | 3mm | UL 94 by SABIC-IP |
Óptico
Property | Value | Comment |
---|---|---|
Transmission | 88 % Show Material materials with Transmission of 88 % | ASTM D 1003 | 2.54 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 39 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 39 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 36 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 36 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Fluid Delivery,Lab Ware and Clinical Diagnostics,Medical Device,Pharmaceutical Packaging & Drug Delivery,Surgical Devices,Wireless Communications | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C |