Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.15 % Show Material materials with Absorción de agua of 0.15 % | ASTM D 570 | 24 Hours |
Absorción de agua, equilibrio | 100.0 °C | 0.58 % Show Material materials with Absorción de agua, equilibrio of 0.58 % | ASTM D 570 | ASTM D 570 |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Rockwell M | 23.0 °C | 70 [-] Show Material materials with Dureza Rockwell M of 70 [-] | ASTM D 785 | ||
Elongación | 23.0 °C | 120 % Show Material materials with Elongación of 120 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 106.8 - 640.8 J/m Show Material materials with Impact strength, Izod notched, ASTM of 106.8 - 640.8 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | ||
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.37 GPa Show Material materials with Módulo elástico of 2.37 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 65 MPa Show Material materials with Resistencia a la tracción of 65 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 23.0 °C | 1250 J/(kg·K) Show Material materials with Calor específico of 1250 J/(kg·K) | ASTM C 351 |
Coeficiente de dilatación térmica | 23.0 °C | 6.84E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 |
Heat deflection temperature, 1.80 MPa | 126 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 126 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Temperatura de reblandecimiento Vicat | 140 °C Show Material materials with Temperatura de reblandecimiento Vicat of 140 °C | ISO 306 | Rate B/120 |
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.96 [-] Show Material materials with Constante dieléctrica of 2.96 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 14.9 kV/mm Show Material materials with Rigidez dieléctrica of 14.9 kV/mm | ASTM D 149 | in air, 3.2 mm |
Óptico
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 25 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 25 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 23 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 23 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components,Fluid Delivery,Lab Ware and Clinical Diagnostics,Medical Device,Monitoring and Imaging,Pharmaceutical Manufacturing,Pharmaceutical Packaging & Drug Delivery,Respiratory,Surgical Devices,Surgical Tray | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-295°C, Nozzle Temperature: 265-290°C, Front - Zone 3 Temperature: 270-295°C, Middle - Zone 2 Temperature: 260-280°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |