General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.08 g/cm³ Show Material materials with Densidad of 1.08 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.2 % Show Material materials with Elongación of 2.2 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 1.4 % Show Material materials with Elongation at yield of 1.4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 68 MPa Show Material materials with Flexural yield strength of 68 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | -30.0 °C | 13 J/m Show Material materials with Impact strength, Izod notched, ASTM of 13 J/m | ASTM D 256 |
23.0 °C | 21 J/m Show Material materials with Impact strength, Izod notched, ASTM of 21 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 3.54 GPa Show Material materials with Módulo de flexión of 3.54 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 3.97 GPa Show Material materials with Módulo elástico of 3.97 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 68 MPa Show Material materials with Resistencia a la tracción of 68 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 1 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 1 kJ/m² | ISO 179/2C |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 1 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 1 kJ/m² | ISO 180/1A |
23.0 °C | 1 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 1 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 87 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 87 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed |
Temperatura de reblandecimiento Vicat | 106 °C Show Material materials with Temperatura de reblandecimiento Vicat of 106 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 78 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 78 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Additive Semiconductor Materials | |
Processing methods | Drying Temperature: 75-85°C, Drying Time (Cumulative): 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 190-220°C, Nozzle Temperature: 190-220°C, Front - Zone 3 Temperature: 190-210°C, Middle - Zone 2 Temperature: 180-200°C, Rear - Zone 1 Temperature: 170-190°C, Mold Temperature: 50-70°C, Screw Speed: 40-70rpm |