General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Material materials with Absorción de agua of 0.08 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.28 g/cm³ Show Material materials with Densidad of 1.28 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 50 % Show Material materials with Elongación of 50 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 3.3 % Show Material materials with Elongation at yield of 3.3 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 73 MPa Show Material materials with Flexural yield strength of 73 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -20.0 °C | 75 J/m Show Material materials with Impact strength, Izod notched, ASTM of 75 J/m | ASTM D 256 | ||
23.0 °C | 90 J/m Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2 GPa Show Material materials with Módulo de flexión of 2 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Material materials with Módulo elástico of 2.4 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 25 MPa Show Material materials with Resistencia a la tracción of 25 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | ||
Impact strength, Izod unnotched, ASTM | No break @ -30°C | ASTM D 4812 | ||||
Resistencia al choque, ensayo Izod no entallado | No break @ -30°C | ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.1E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9.7E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 46 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 46 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 165 °C Show Material materials with Temperatura de reblandecimiento Vicat of 165 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Velocidad de flujo del volumen derretido | 26 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 26 cm³/10min | ISO 1133 | 250°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components,Enclosures,Photovoltaic Components | |
| Processing methods | Drying Temperature: 60-75°C, Drying Time: 4-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.05%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |