General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.5 g/cm³ Show Material materials with Densidad of 1.5 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Material materials with Elongación of 2.5 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 4.2 % Show Material materials with Flexural strain of 4.2 % | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 96 J/m Show Material materials with Impact strength, Izod notched, ASTM of 96 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 817 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 817 J/m | ASTM D 4812 |
Límite elástico | 23.0 °C | 112 MPa Show Material materials with Límite elástico of 112 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 7.4 GPa Show Material materials with Módulo de flexión of 7.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 8.84 GPa Show Material materials with Módulo elástico of 8.84 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 175 MPa Show Material materials with Resistencia a la flexión of 175 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 11 kJ/m² | ISO 180/1A |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 52 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 52 kJ/m² | ISO 180/1U |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed |
Temperatura de reblandecimiento Vicat | 204 °C Show Material materials with Temperatura de reblandecimiento Vicat of 204 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 - 0.8 % Show Material materials with Contracción of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1 - 1.2 % Show Material materials with Contracción transversal of 1 - 1.2 % | SABIC method |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 | 250°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Electronic Components | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 60-75°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.05%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |