Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.13 g/cm³ Show Material materials with Densidad of 1.13 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 10 % Show Material materials with Elongación of 10 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 93 MPa Show Material materials with Hardness, Ball Indentation of 93 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 116 [-] Show Material materials with Hardness, Rockwell R of 116 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ISO 527 | 50 mm/min |
Módulo de flexión | 23.0 °C | 2.4 GPa Show Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.3 GPa Show Material materials with Módulo elástico of 2.3 GPa | ISO 527 | 1 mm/min |
Resistencia a la tracción | 23.0 °C | 45 MPa Show Material materials with Resistencia a la tracción of 45 MPa | ISO 527 | 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/1eA |
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 20 kJ/m² | ISO 180/1A |
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 45 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 97 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 97 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 124 °C Show Material materials with Temperatura de reblandecimiento Vicat of 124 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | FMVSS Burning Speed, thickness 1 mm | 35mm/min | FMVSS 302 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.6 [-] Show Material materials with Constante dieléctrica of 2.6 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 9E-3 [-] Show Material materials with Factor de disipación of 9E-3 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 275 V Show Material materials with Índice de seguimiento comparativo of 275 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo del volumen derretido | 20 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 20 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Conditioning,Audio,Auto Aftermarket,Body Protection,Cladding,Cluster,Console,Data Management,Data Transfer,Defense Vehicles,Dishwasher,Displays,Document Handling,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,Exterior,Forward Lighting,Freezer,Glove Box,Headliner,Infotainment/Telematic,Interior,Medical Device,Neighborhood Electric Vehicle,Non-LED Lighting,Overhead,Personal Computing,Rear/Signal Lighting,Recreational Vehicle,Seat,Small Appliance,Storage/Table,Structure,Trim,Wireless Communications | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 275-300°C, Nozzle Temperature: 275-300°C, Front - Zone 3 Temperature: 260-300°C, Middle - Zone 2 Temperature: 255-295°C, Rear - Zone 1 Temperature: 250-290°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |