General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.15 % Show Material materials with Absorción de agua of 0.15 % | ISO 62 | 23°C, 50% RH |
Absorción de agua, equilibrio | 100.0 °C | 0.58 % Show Material materials with Absorción de agua, equilibrio of 0.58 % | ASTM D 570 |
Densidad | 23.0 °C | 1.2 g/cm³ Show Material materials with Densidad of 1.2 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 77 % Show Material materials with Elongación of 77 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min | ||
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m | ASTM D 256 | ||
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ISO 527 | 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.25 GPa Show Material materials with Módulo de flexión of 2.25 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.23 GPa Show Material materials with Módulo elástico of 2.23 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 58 MPa Show Material materials with Resistencia a la tracción of 58 MPa | ISO 527 | 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 68 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 68 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 11 kJ/m² | ISO 180/1A | ||
23.0 °C | 65 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 65 kJ/m² | ISO 180/1A | |||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1260 J/(kg·K) Show Material materials with Calor específico of 1260 J/(kg·K) | ASTM C 351 | ||
Coeficiente de dilatación térmica | 23.0 °C | 6.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 | ||
Heat deflection temperature, 1.80 MPa | 125 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ISO 75/Af | 1.8 MPa | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |||
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 142 °C Show Material materials with Temperatura de reblandecimiento Vicat of 142 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.96 [-] Show Material materials with Constante dieléctrica of 2.96 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 15 kV/mm Show Material materials with Rigidez dieléctrica of 15 kV/mm | ASTM D 149 | in air, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Óptico
Property | Value | Comment |
---|---|---|
Índice de refracción | 1.59 [-] Show Material materials with Índice de refracción of 1.59 [-] | ISO 489 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.6 - 0.8 % Show Material materials with Contracción of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | ATM/Ticket Machine,Enclosure/Housing/Cover,Enclosures,Lab Ware and Clinical Diagnostics,LED Lighting,Non-LED Lighting,Personal Computing,Wireless Communications | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C |