| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 150 % Show Material materials with Elongación of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 8.6 % Show Material materials with Elongation at yield of 8.6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 72 MPa Show Material materials with Flexural yield strength of 72 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 427 J/m Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m | ASTM D 256 |
23.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Material materials with Módulo de flexión of 2.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.13 GPa Show Material materials with Módulo elástico of 2.13 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 44 MPa Show Material materials with Resistencia a la tracción of 44 MPa | ASTM D 638 | Type I, 50 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 |
Heat deflection temperature, 1.80 MPa | 99 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 99 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 112 °C Show Material materials with Temperatura de reblandecimiento Vicat of 112 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción transversal of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo de la masa derretida | 14 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 14 g/10min | ASTM D 1238 | 260°C/5.0 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique,Audio,Auto Aftermarket,Circuit Protection,Cladding,Console,Cooking Range,Data Management,Data Transfer,Displays,Document Handling,Door Handle,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior Trim,Exterior,Fixture Bath/Shower,Forward Lighting,Freezer,Front Grille,Infotainment/Telematic,Interior,Lawn/Garden,LED Lighting,Medical Device,Non-LED Lighting,Personal Computing,Pharmaceutical Packaging & Drug Delivery,Rail Cabin Interiors,Rear/Signal Lighting,Recreational Vehicle,Refrigerator,Small Appliance,Spoiler,Toy,Trim,Wheel Cover,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 100-105°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 255-290°C, Middle - Zone 2 Temperature: 255-290°C, Rear - Zone 1 Temperature: 250-280°C, Mold Temperature: 75-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |