General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | ASTM D 570 | 24 Hours |
Absorción de agua, equilibrio | 23.0 °C | 0.4 % Show Material materials with Absorción de agua, equilibrio of 0.4 % | ASTM D 570 |
Densidad | 23.0 °C | 1.13 g/cm³ Show Material materials with Densidad of 1.13 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 100 % Show Material materials with Elongación of 100 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 77 MPa Show Material materials with Flexural yield strength of 77 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 427 J/m Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m | ASTM D 256 |
23.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 52 MPa Show Material materials with Límite elástico of 52 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.06 GPa Show Material materials with Módulo de flexión of 2.06 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.06 GPa Show Material materials with Módulo elástico of 2.06 GPa | ASTM D 638 | 50 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8.1E-5 1/K | ASTM E 831 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 |
Heat deflection temperature, 1.80 MPa | 104 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de fusión | 245 - 260 °C Show Material materials with Temperatura de fusión of 245 - 260 °C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.7 % Show Material materials with Contracción of 0.4 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Enclosures | |
| Processing methods | Drying Temperature: 100-110°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 24hrs, Maximum Moisture Content: 0.04-0.05%, Minimum Moisture Content: 0.04%, Barrel - Zone 1 Temperature: 240-250°C, Barrel - Zone 2 Temperature: 240-255°C, Barrel - Zone 3 Temperature: 240-255°C, Barrel - Zone 4 Temperature: 240-255°C, Adapter - Zone 5 Temperature: 245-260°C, Head - Zone 6 - Top Temperature: 245-260°C, Head - Zone 7 - Bottom Temperature: 245-260°C, Screw Speed: 20-50rpm, Extruder Feed Zone Temperature: 60-80°C, Mold Temperature: 40-90°C, Die Temperature: 250-265°C | |