General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | ASTM D 570 | 24 Hours |
Absorción de agua, equilibrio | 23.0 °C | 0.4 % Show Material materials with Absorción de agua, equilibrio of 0.4 % | ASTM D 570 |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 120 % Show Material materials with Elongación of 120 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 9 % Show Material materials with Elongation at yield of 9 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 106 J/m Show Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 |
23.0 °C | 427 J/m Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 2.96 GPa Show Material materials with Módulo de flexión of 2.96 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 58 MPa Show Material materials with Resistencia a la tracción of 58 MPa | ASTM D 638 | Type I, 5 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.66E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.66E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.1E-5 1/K | ASTM E 831 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 |
Heat deflection temperature, 1.80 MPa | 126 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 126 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Temperatura de reblandecimiento Vicat | 117 °C Show Material materials with Temperatura de reblandecimiento Vicat of 117 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.6 % Show Material materials with Contracción of 0.4 - 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 10 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 10 g/10min | ASTM D 1238 | 260°C/5.0 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique,Auto Aftermarket,Personal Computing,Trim,Wireless Communications | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-300°C, Front - Zone 3 Temperature: 270-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 260-270°C, Mold Temperature: 75-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |