General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.04 g/cm³ Show Material materials with Densidad of 1.04 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 62 MPa Show Material materials with Flexural yield strength of 62 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 42 J/m Show Material materials with Impact strength, Izod notched, ASTM of 42 J/m | ASTM D 256 |
23.0 °C | 245 J/m Show Material materials with Impact strength, Izod notched, ASTM of 245 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 40 MPa Show Material materials with Límite elástico of 40 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 2.06 GPa Show Material materials with Módulo de flexión of 2.06 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.13 GPa Show Material materials with Módulo elástico of 2.13 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 33 MPa Show Material materials with Resistencia a la tracción of 33 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 18 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 18 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 18 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 18 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.36E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.36E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.36E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9.36E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 82 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 82 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 98 °C Show Material materials with Temperatura de reblandecimiento Vicat of 98 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción transversal of 0.5 - 0.8 % | SABIC method |
Velocidad de flujo de la masa derretida | 6 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6 g/10min | ASTM D 1238 | 200°C/3.8 kgf | |
Velocidad de flujo del volumen derretido | 24 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 24 cm³/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Bottles,Cluster,Doors Hardware/Trim,Exterior,Front Grille,Heavy Vehicles,Interior,Lawn/Garden,Recreational Vehicle,Seat,Trim | |
Processing methods | Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 230-275°C, Nozzle Temperature: 230-275°C, Front - Zone 3 Temperature: 230-245°C, Middle - Zone 2 Temperature: 215-225°C, Rear - Zone 1 Temperature: 200-210°C, Mold Temperature: 25-60°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm |