Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.15 % Show Material materials with Absorción de agua of 0.15 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 125 % Show Material materials with Elongación of 125 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6.3 % Show Material materials with Elongation at yield of 6.3 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 14 J/m Show Material materials with Impact strength, Izod notched, ASTM of 14 J/m | ASTM D 256 | ||
23.0 °C | 918 J/m Show Material materials with Impact strength, Izod notched, ASTM of 918 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.2 GPa Show Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.27 GPa Show Material materials with Módulo elástico of 2.27 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 72 MPa Show Material materials with Resistencia a la tracción of 72 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO 179/1eA | ||
23.0 °C | 75 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 75 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 70 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.74E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.74E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.74E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.74E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 150 °C Show Material materials with Temperatura de reblandecimiento Vicat of 150 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 - 0.8 % Show Material materials with Contracción of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción transversal of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo de la masa derretida | 7.4 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 7.4 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Management,Personal Care | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |