General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.35 % Show Material materials with Absorción de agua of 0.35 % | ISO 62 |
Absorción de agua, equilibrio | 23.0 °C | 0.35 % Show Material materials with Absorción de agua, equilibrio of 0.35 % | ASTM D 570 |
Densidad | 23.0 °C | 1.2 g/cm³ Show Material materials with Densidad of 1.2 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Límite elástico | 23.0 °C | 60 MPa Show Material materials with Límite elástico of 60 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.35 GPa Show Material materials with Módulo elástico of 2.35 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 15 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ASTM E 831 | -40°C to 95°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 |
Heat deflection temperature, 0.45 MPa | 132 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 132 °C | ISO 75/Bf | 0.45 MPa | |
Temperatura de reblandecimiento Vicat | 138 °C Show Material materials with Temperatura de reblandecimiento Vicat of 138 °C | ASTM D 1525 | Rate B/50 |
Eléctrico
Óptico
| Property | Value | Comment |
|---|---|---|
Índice de refracción | 1.59 [-] Show Material materials with Índice de refracción of 1.59 [-] | ISO 489 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method |
Velocidad de flujo de la masa derretida | 8.9 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 8.9 g/10min | ASTM D 1238 | 250°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 8 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 8 cm³/10min | ISO 1133 | 250°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Management | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 340-370°C, Nozzle Temperature: 340-370°C, Front - Zone 3 Temperature: 350-380°C, Middle - Zone 2 Temperature: 320-340°C, Rear - Zone 1 Temperature: 270-290°C, Hopper Temperature: 60-80°C, Mold Temperature: 75-95°C | |