Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.39 g/cm³ Show Material materials with Densidad of 1.39 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 3 % Show Material materials with Elongación of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural strain | 23.0 °C | 3 % Show Material materials with Flexural strain of 3 % | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 120 MPa Show Material materials with Flexural yield strength of 120 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 160 MPa Show Material materials with Hardness, Ball Indentation of 160 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 85 MPa Show Material materials with Límite elástico of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 4.8 GPa Show Material materials with Módulo de flexión of 4.8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 5.3 GPa Show Material materials with Módulo elástico of 5.3 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 120 MPa Show Material materials with Resistencia a la flexión of 120 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 85 MPa Show Material materials with Resistencia a la tracción of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/2C |
23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/2C | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 20 kJ/m² | ISO 179/2C |
23.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 30 kJ/m² | ISO 179/2C | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A |
23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 20 kJ/m² | ISO 180/1U |
23.0 °C | 28 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 28 kJ/m² | ISO 180/1U | |
Aplicaciones térmicas
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.2 - 0.6 % Show Material materials with Contracción of 0.2 - 0.6 % | SABIC method |
Melt viscosity | 260.0 °C | 90 Pa·s Show Material materials with Melt viscosity of 90 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Velocidad de flujo del volumen derretido | 40 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 40 cm³/10min | ISO 1133 | 250°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |