Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Material materials with Absorción de agua of 0.08 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.29 g/cm³ Show Material materials with Densidad of 1.29 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 160 % Show Material materials with Elongación of 160 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 25 J/m Show Material materials with Impact strength, Izod notched, ASTM of 25 J/m | ASTM D 256 |
23.0 °C | 59 J/m Show Material materials with Impact strength, Izod notched, ASTM of 59 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 48 MPa Show Material materials with Límite elástico of 48 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.5 GPa Show Material materials with Módulo elástico of 2.5 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 31 MPa Show Material materials with Resistencia a la tracción of 31 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.18E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.18E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.9E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Temperatura de reblandecimiento Vicat | 156 °C Show Material materials with Temperatura de reblandecimiento Vicat of 156 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.9 [-] Show Material materials with Constante dieléctrica of 2.9 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | ASTM D 150 | at 1 MHz |
Resistividad eléctrica | 23.0 °C | 1.00E+15 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+15 Ω·m | ASTM D 257 |
Rigidez dieléctrica | 23.0 °C | 15.9 kV/mm Show Material materials with Rigidez dieléctrica of 15.9 kV/mm | ASTM D 149 | in air, 0.8 mm |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 2.1 - 2.3 % Show Material materials with Contracción of 2.1 - 2.3 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 2.1 - 2.3 % Show Material materials with Contracción transversal of 2.1 - 2.3 % | SABIC method |
Velocidad de flujo de la masa derretida | 17 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 17 g/10min | ASTM D 1238 | 250°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 16 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 16 cm³/10min | ISO 1133 | 250°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Medical Device,Wireless Communications, hinge applications. | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |