Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Material materials with Absorción de agua of 0.08 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.31 g/cm³ Show Material materials with Densidad of 1.31 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 15 % Show Material materials with Elongación of 15 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 3.5 % Show Material materials with Elongation at yield of 3.5 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 65 MPa Show Material materials with Límite elástico of 65 MPa | ISO 527 | 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.6 GPa Show Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.8 GPa Show Material materials with Módulo elástico of 2.8 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 50 MPa Show Material materials with Resistencia a la tracción of 50 MPa | ISO 527 | 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 3 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3 kJ/m² | ISO 179/1eA | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A | ||
23.0 °C | 2 - 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 - 4 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No break @ 23,-30°C | ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75/Ae | 1.8 MPa | |||
Temperatura de reblandecimiento Vicat | 185 °C Show Material materials with Temperatura de reblandecimiento Vicat of 185 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.1 [-] Show Material materials with Constante dieléctrica of 3.1 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 16 kV/mm Show Material materials with Rigidez dieléctrica of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.1 - 1.8 % Show Material materials with Contracción of 1.1 - 1.8 % | SABIC method |
Contracción transversal | 23.0 °C | 0.9 - 1.8 % Show Material materials with Contracción transversal of 0.9 - 1.8 % | SABIC method |
Velocidad de flujo del volumen derretido | 20 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 20 cm³/10min | ISO 1133 | 250°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components,Wiring Devices | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |