Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.04 % Show Material materials with Absorción de agua of 0.04 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.28 g/cm³ Show Material materials with Densidad of 1.28 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 7 % Show Material materials with Elongación of 7 % | ISO 527 | 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 205 J/m Show Material materials with Impact strength, Izod notched, ASTM of 205 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1600 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1600 J/m | ASTM D 4812 |
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 3.5 GPa Show Material materials with Módulo de flexión of 3.5 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 3.8 GPa Show Material materials with Módulo elástico of 3.8 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | ASTM D 638 | Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 95 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 95 kJ/m² | ISO 179/1eU |
23.0 °C | 95 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 95 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A |
23.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 14 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 74 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 74 kJ/m² | ISO 180/1U |
23.0 °C | 110 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 110 kJ/m² | ISO 180/1U | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 101 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 101 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 118 °C Show Material materials with Temperatura de reblandecimiento Vicat of 118 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 0.4mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.15 - 0.25 % Show Material materials with Contracción of 0.15 - 0.25 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.3 - 0.4 % Show Material materials with Contracción transversal of 0.3 - 0.4 % | SABIC method |
Velocidad de flujo del volumen derretido | 26 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 26 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wireless Communications | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 255-290°C, Middle - Zone 2 Temperature: 255-290°C, Rear - Zone 1 Temperature: 250-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |