Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.14 % Show Material materials with Absorción de agua of 0.14 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.27 g/cm³ Show Material materials with Densidad of 1.27 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 150 % Show Material materials with Elongación of 150 % | ASTM D 638 | Type I, 5 mm/min | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 105 MPa Show Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 120 J/m Show Material materials with Impact strength, Izod notched, ASTM of 120 J/m | ASTM D 256 | ||
23.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 56 MPa Show Material materials with Límite elástico of 56 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Módulo de flexión | 23.0 °C | 2.9 GPa Show Material materials with Módulo de flexión of 2.9 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 3.4 GPa Show Material materials with Módulo elástico of 3.4 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 60 MPa Show Material materials with Resistencia a la tracción of 60 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 40 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | ||
23.0 °C | 15 - 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 15 - 45 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No break @ 23,-30°C | ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 |
Heat deflection temperature, 0.45 MPa | 119 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 119 °C | ISO 75/Bf | 0.45 MPa | |
Temperatura de reblandecimiento Vicat | 133 °C Show Material materials with Temperatura de reblandecimiento Vicat of 133 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.7 - 0.9 % Show Material materials with Contracción of 0.7 - 0.9 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 7 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 | 265°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Exterior Trim | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C | |