Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.14 % Show Material materials with Absorción de agua of 0.14 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 120 % Show Material materials with Elongación of 120 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 100 J/m Show Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 |
23.0 °C | 700 J/m Show Material materials with Impact strength, Izod notched, ASTM of 700 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 58 MPa Show Material materials with Límite elástico of 58 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.03 GPa Show Material materials with Módulo de flexión of 2.03 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.47 GPa Show Material materials with Módulo elástico of 2.47 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 66 MPa Show Material materials with Resistencia a la tracción of 66 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.5E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 113 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 113 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 130 °C Show Material materials with Temperatura de reblandecimiento Vicat of 130 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.7 - 0.8 % Show Material materials with Contracción of 0.7 - 0.8 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 12.5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 12.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 10 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 10 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Medical Device,Personal Computing,Swimming Pool/Spa,Washing Machine | |
| Processing methods | Drying Temperature: 85-100°C, Drying Time: 2-3hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 280-290°C, Front - Zone 3 Temperature: 290-300°C, Middle - Zone 2 Temperature: 280-290°C, Rear - Zone 1 Temperature: 275-285°C, Hopper Temperature: 50°C, Mold Temperature: 65-75°C, Back Pressure: 0.1-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80% | |