Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 100 % Show Material materials with Elongación of 100 % | ASTM D 638 | Type I, 5 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 120 J/m Show Material materials with Impact strength, Izod notched, ASTM of 120 J/m | ASTM D 256 | ||
23.0 °C | 500 J/m Show Material materials with Impact strength, Izod notched, ASTM of 500 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 60 MPa Show Material materials with Límite elástico of 60 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Módulo de flexión | 23.0 °C | 3.1 GPa Show Material materials with Módulo de flexión of 3.1 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 3.4 GPa Show Material materials with Módulo elástico of 3.4 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 55 MPa Show Material materials with Resistencia a la tracción of 55 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 40 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No break @ 23,-30°C | ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 |
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 138 °C Show Material materials with Temperatura de reblandecimiento Vicat of 138 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.7 - 0.8 % Show Material materials with Contracción of 0.7 - 0.8 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 11 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 11 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 9 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 9 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket | |
| Processing methods | Drying Temperature: 120-110°C, Drying Time: 2-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-300°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 270-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 260-270°C, Mold Temperature: 60-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |