General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 20 % Show Material materials with Elongación of 20 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 82 MPa Show Material materials with Flexural yield strength of 82 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 92 MPa Show Material materials with Hardness, Ball Indentation of 92 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 111 [-] Show Material materials with Hardness, Rockwell R of 111 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ISO 527 | 50 mm/min |
Módulo de flexión | 23.0 °C | 2.5 GPa Show Material materials with Módulo de flexión of 2.5 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.46 GPa Show Material materials with Módulo elástico of 2.46 GPa | ISO 527 | 1 mm/min |
Resistencia a la tracción | 23.0 °C | 43 MPa Show Material materials with Resistencia a la tracción of 43 MPa | ISO 527 | 50 mm/min |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A |
23.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 20 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.5E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 86 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 86 °C | ISO 75/Ae | 1.8 MPa | |||
Temperatura de reblandecimiento Vicat | 107 °C Show Material materials with Temperatura de reblandecimiento Vicat of 107 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating | 3.2mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.6 % Show Material materials with Contracción of 0.4 - 0.6 % | SABIC method |
Velocidad de flujo del volumen derretido | 20 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 20 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Front Grille,Spoiler | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.05%, Melt Temperature: 250-270°C, Nozzle Temperature: 230-260°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 230-260°C, Rear - Zone 1 Temperature: 220-250°C, Hopper Temperature: 60-80°C, Mold Temperature: 50-70°C | |