General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.09 g/cm³ Show Material materials with Densidad of 1.09 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 38 % Show Material materials with Elongación of 38 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.4 % Show Material materials with Elongation at yield of 3.4 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 56 MPa Show Material materials with Flexural yield strength of 56 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 70 J/m Show Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 |
23.0 °C | 195 J/m Show Material materials with Impact strength, Izod notched, ASTM of 195 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 36 MPa Show Material materials with Límite elástico of 36 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 1.87 GPa Show Material materials with Módulo de flexión of 1.87 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 1.91 GPa Show Material materials with Módulo elástico of 1.91 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 32 MPa Show Material materials with Resistencia a la tracción of 32 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 13 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.09E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.09E-4 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 69 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 69 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 85 °C Show Material materials with Temperatura de reblandecimiento Vicat of 85 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.3 - 0.7 % Show Material materials with Contracción of 0.3 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 9.7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 9.7 g/10min | ASTM D 1238 | 220°C/10 kg | |
Velocidad de flujo del volumen derretido | 2 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 2 cm³/10min | ISO 1133 | 220°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Building Accessory,Building/Construction Sheet,Cladding/Roof,Enclosures,Heavy Vehicles,Window | |
Processing methods | Drying Temperature: 85-95°C, Drying Time: 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 190-210°C, Barrel - Zone 1 Temperature: 180-200°C, Barrel - Zone 2 Temperature: 180-200°C, Barrel - Zone 3 Temperature: 180-205°C, Barrel - Zone 4 Temperature: 180-205°C, Hopper Temperature: 60-80°C, Adapter Temperature: 180-205°C, Die Temperature: 185-205°C |