Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.15 g/cm³ Show Material materials with Densidad of 1.15 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 21 % Show Material materials with Elongación of 21 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 70 MPa Show Material materials with Flexural yield strength of 70 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 27 J/m Show Material materials with Impact strength, Izod notched, ASTM of 27 J/m | ASTM D 256 |
23.0 °C | 49 J/m Show Material materials with Impact strength, Izod notched, ASTM of 49 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 50 MPa Show Material materials with Límite elástico of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.41 GPa Show Material materials with Módulo de flexión of 2.41 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.47 GPa Show Material materials with Módulo elástico of 2.47 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 36 MPa Show Material materials with Resistencia a la tracción of 36 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 3 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 3 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8.1E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.8E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 73 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 73 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Temperatura de reblandecimiento Vicat | 78 °C Show Material materials with Temperatura de reblandecimiento Vicat of 78 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.3 - 0.6 % Show Material materials with Contracción of 0.3 - 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 38 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 38 g/10min | ASTM D 1238 | 220°C/10 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Cladding/Roof,Photovoltaic Components,Window | |
| Processing methods | Drying Temperature: 75-85°C, Drying Time: 4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 200-230°C, Barrel - Zone 1 Temperature: 205-220°C, Barrel - Zone 2 Temperature: 210-225°C, Barrel - Zone 3 Temperature: 215-225°C, Barrel - Zone 4 Temperature: 215-225°C, Hopper Temperature: 60-80°C, Adapter Temperature: 200-225°C, Die Temperature: 210-225°C | |