General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.5 g/cm³ Show Material materials with Densidad of 1.5 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 3.1 % Show Material materials with Elongación of 3.1 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 5.96 GPa Show Material materials with Módulo elástico of 5.96 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 100 MPa Show Material materials with Resistencia a la tracción of 100 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 6.2 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6.2 kJ/m² | ISO 179/1eA |
23.0 °C | 6.2 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6.2 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 30.1 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 30.1 kJ/m² | ISO 179/1eU |
23.0 °C | 31.8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 31.8 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |
Temperatura de fusión | 223 °C Show Material materials with Temperatura de fusión of 223 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 40mil: 775 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 600 °C, FMVSS Class: DNI - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 200 V Show Material materials with Índice de seguimiento comparativo of 200 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |