General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.4 % Show Material materials with Absorción de agua of 0.4 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.37 g/cm³ Show Material materials with Densidad of 1.37 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 3.3 % Show Material materials with Elongación of 3.3 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 115 [-] Show Material materials with Hardness, Rockwell R of 115 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 4.7 GPa Show Material materials with Módulo de flexión of 4.7 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5.2 GPa Show Material materials with Módulo elástico of 5.2 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 150 MPa Show Material materials with Resistencia a la flexión of 150 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 95 MPa Show Material materials with Resistencia a la tracción of 95 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 30 kJ/m² | ISO 179/1eU |
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 60 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 30 kJ/m² | ISO 180/1U |
-30.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 40 kJ/m² | ISO 180/1U | |
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 45 kJ/m² | ISO 180/1U | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 6 kJ/m² | ISO 180/1A |
-30.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A | |
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1860 J/(kg·K) Show Material materials with Calor específico of 1860 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 4.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4.1E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 225 °C Show Material materials with Temperatura de fusión of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Oxygen index: 20 %, Glow Wire Flammability Index, 120mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.6 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.6 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 42 kV/mm Show Material materials with Rigidez dieléctrica of 42 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 350 V Show Material materials with Índice de seguimiento comparativo of 350 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Material materials with Contracción of 0.5 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.1 % Show Material materials with Contracción transversal of 1.1 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 27 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 27 g/10min | ISO 1133 | 250°C/2.16kg | |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |