Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.31 g/cm³ Show Material materials with Densidad of 1.31 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |
Elongation at yield | 23.0 °C | 10 % Show Material materials with Elongation at yield of 10 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 57 MPa Show Material materials with Límite elástico of 57 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.5 GPa Show Material materials with Módulo de flexión of 2.5 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 2.6 GPa Show Material materials with Módulo elástico of 2.6 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 2.9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2.9 kJ/m² | ISO 179/1eA |
23.0 °C | 3.4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.4 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 276 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 276 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 3.8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 3.8 kJ/m² | ISO 180/1A |
23.0 °C | 4.2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.2 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.9E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.9E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 147 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 147 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 65 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO 75-1/-2 | annealed | |||
Temperatura de fusión | 223 °C Show Material materials with Temperatura de fusión of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | FMVSS Class: SE | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 2 % Show Material materials with Contracción of 2 % | ISO 294-4 | Annealed |
Contracción transversal | 23.0 °C | 2 % Show Material materials with Contracción transversal of 2 % | ISO 294-4 | Annealed |
Velocidad de flujo de la masa derretida | 34 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 34 g/10min | ISO 1133 | 250°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |