| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.67 g/cm³ Show Material materials with Densidad of 1.67 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 1 % Show Material materials with Elongación of 1 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 8.3 GPa Show Material materials with Módulo de flexión of 8.3 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 7.1 GPa Show Material materials with Módulo elástico of 7.1 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 57 MPa Show Material materials with Resistencia a la flexión of 57 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 39 MPa Show Material materials with Resistencia a la tracción of 39 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 2.4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2.4 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 7.9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 7.9 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 2.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 2.8E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 197 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 197 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ISO 75-1/-2 | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, Glow Wire Ignition Temperature, 60mil: 675 °C, Glow Wire Ignition Temperature, 120mil: 750 °C | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+8 Ω·cm Show Material materials with Volume resistivity of 1.00E+8 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 40% Carbon Powder | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Max. regrind level: 15%, Melt Temperature Optimum: 275°C, Min. melt temperature: 260°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |