General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.4 % Show Material materials with Absorción de agua of 0.4 % | Sim. to ISO 62 | 80mil |
Coefficient of friction | 0.4 [-] Show Material materials with Coefficient of friction of 0.4 [-] | ASTM 1894 | against steel | |
Densidad | 23.0 °C | 1.31 g/cm³ Show Material materials with Densidad of 1.31 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |||
Elongación | 23.0 °C | 40 % Show Material materials with Elongación of 40 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527-1/-2 | ||
Hardness, Ball Indentation | 23.0 °C | 139 MPa Show Material materials with Hardness, Ball Indentation of 139 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 2.2 GPa Show Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.5 GPa Show Material materials with Módulo elástico of 2.5 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 85 MPa Show Material materials with Resistencia a la flexión of 85 MPa | ISO 178 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.5 kJ/m² | ISO 180/1A | ||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Izod entallado | No Break @ 23°C, ISO 179/1eU | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 2110 J/(kg·K) Show Material materials with Calor específico of 2110 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.9E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.9E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 2E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Conductividad térmica | 23.0 °C | 0.29 W/(m·K) Show Material materials with Conductividad térmica of 0.29 W/(m·K) | of solid | ||
Heat deflection temperature, 0.45 MPa | 180 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | annealed | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | 240mil | |||
Temperatura de fusión | 225 °C Show Material materials with Temperatura de fusión of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 175 °C Show Material materials with Temperatura de reblandecimiento Vicat of 175 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 55 °C Show Material materials with Temperatura de transición del vidrio of 55 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 22 %, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, FMVSS Class: SE - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.2 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.2 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.6 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.6 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 7.9E-4 [-] Show Material materials with Dissipation factor, 100Hz of 7.9E-4 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 26 kV/mm Show Material materials with Rigidez dieléctrica of 26 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+12 Ω/sq Show Material materials with Surface resistivity of 1.00E+12 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 575 V Show Material materials with Índice de seguimiento comparativo of 575 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.7 % Show Material materials with Contracción of 1.7 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.6 % Show Material materials with Contracción transversal of 1.6 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 19 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 19 g/10min | ISO 1133 | 250°C/2.16kg | |
Velocidad de flujo del volumen derretido | 14 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 14 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |