Propiedades
General
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |||
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | min. | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527-1/-2 | ||
Hardness, Ball Indentation | 23.0 °C | 139 MPa Show Material materials with Hardness, Ball Indentation of 139 MPa | ISO 2039-1 | ||
Límite elástico | 23.0 °C | 57 MPa Show Material materials with Límite elástico of 57 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 2.4 GPa Show Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.6 GPa Show Material materials with Módulo elástico of 2.6 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 85 MPa Show Material materials with Resistencia a la flexión of 85 MPa | ISO 178 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 130 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 2100 J/(kg·K) Show Material materials with Calor específico of 2100 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 180 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | annealed | |||
Temperatura de fusión | 223 °C Show Material materials with Temperatura de fusión of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 175 °C Show Material materials with Temperatura de reblandecimiento Vicat of 175 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 55 °C Show Material materials with Temperatura de transición del vidrio of 55 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: SE - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.7 % Show Material materials with Contracción of 1.7 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.7 % Show Material materials with Contracción transversal of 1.7 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 10 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 10 g/10min | ISO 1133 | 250°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |