Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.31 % Show Material materials with Absorción de agua of 0.31 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.42 [-] Show Material materials with Coeficiente de Poisson of 0.42 [-] | |||
Elongación | 23.0 °C | 150 % Show Material materials with Elongación of 150 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 104 [-] Show Material materials with Hardness, Rockwell R of 104 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 38 MPa Show Material materials with Límite elástico of 38 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 1.55 GPa Show Material materials with Módulo de flexión of 1.55 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 1.7 GPa Show Material materials with Módulo elástico of 1.7 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 50 MPa Show Material materials with Resistencia a la flexión of 50 MPa | ISO 178 | ||
Resistencia a la tracción | 23.0 °C | 30 MPa Show Material materials with Resistencia a la tracción of 30 MPa | ISO 527-1/-2 | 50mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |||
23.0 °C | 85 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 85 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 270 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 270 kJ/m² | No Break @ 23,-30°C, ISO180/1A | ||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A | ||
-30.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 15 kJ/m² | ISO 180/1A | |||
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 60 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2100 J/(kg·K) Show Material materials with Calor específico of 2100 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 2.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.9E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.9E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | 30mil | |||
Temperatura de fusión | 225 °C Show Material materials with Temperatura de fusión of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 125 °C Show Material materials with Temperatura de reblandecimiento Vicat of 125 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, Oxygen index: 19 %, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Flammability Index, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.4 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 27 kV/mm Show Material materials with Rigidez dieléctrica of 27 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 2.5 % Show Material materials with Contracción of 2.5 % | ISO 294-4 | Annealed |
Contracción transversal | 23.0 °C | 1.9 % Show Material materials with Contracción transversal of 1.9 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 5 g/10min | ISO 1133 | 250°C/5kg |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |