General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.6 % Show Material materials with Absorción de agua of 0.6 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.18 g/cm³ Show Material materials with Densidad of 1.18 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 55 [-] Show Material materials with Dureza Shore D of 55 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 600 % Show Material materials with Elongación of 600 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 43 % Show Material materials with Elongation at yield of 43 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 15 MPa Show Material materials with Límite elástico of 15 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 0.43 GPa Show Material materials with Módulo de flexión of 0.43 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.37 GPa Show Material materials with Módulo elástico of 0.37 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 130 kN/m Show Material materials with Resistencia a desgarros of 130 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 105 kN/m Show Material materials with Resistencia a desgarros transversal of 105 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 130 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 120 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 120 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |||
Coeficiente de dilatación térmica | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 50 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 50 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 40 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 40 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 222 °C Show Material materials with Temperatura de fusión of 222 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 170 °C Show Material materials with Temperatura de reblandecimiento Vicat of 170 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -55 °C Show Material materials with Temperatura de transición del vidrio of -55 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Oxygen index: 22 %, FMVSS Class: SE -, Burning rate, Thickness 1 mm: 23 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 4.4 [-] Show Material materials with Constante dieléctrica, 1 MHz of 4.4 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.6 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.6 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 20 kV/mm Show Material materials with Rigidez dieléctrica of 20 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 5.00E+14 Ω/sq Show Material materials with Surface resistivity of 5.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.4 % Show Material materials with Contracción of 1.4 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.5 % Show Material materials with Contracción transversal of 1.5 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 15 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 15 g/10min | ISO 1133 | 240°C/2.16kg | |
Velocidad de flujo del volumen derretido | 14 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 14 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 55°C | |