General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.42 [-] Show Material materials with Coeficiente de Poisson of 0.42 [-] | |||
Elongación | 23.0 °C | 130 % Show Material materials with Elongación of 130 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 36 MPa Show Material materials with Límite elástico of 36 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 1.5 GPa Show Material materials with Módulo de flexión of 1.5 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 1.6 GPa Show Material materials with Módulo elástico of 1.6 GPa | ISO 527-1/-2 | ||
Resistencia a la flexión | 23.0 °C | 50 MPa Show Material materials with Resistencia a la flexión of 50 MPa | ISO 178 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 85 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 85 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 60 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Izod entallado | No Break @ 23,-30°C, ISO180/1A |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75-1/-2 | annealed | |
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |
Temperatura de fusión | 225 °C Show Material materials with Temperatura de fusión of 225 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |