General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |||
Dureza Rockwell M | 23.0 °C | 88.7 [-] Show Material materials with Dureza Rockwell M of 88.7 [-] | ISO 2039-2 | ||
Elongación | 23.0 °C | 40 % Show Material materials with Elongación of 40 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 20 % Show Material materials with Elongation at yield of 20 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 73 MPa Show Material materials with Límite elástico of 73 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 3.1 GPa Show Material materials with Módulo de flexión of 3.1 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 3.1 GPa Show Material materials with Módulo elástico of 3.1 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 8.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8.5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 9.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9.5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23°C, ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 159 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 159 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 92 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 92 °C | ISO 75-1/-2 | |
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 174 °C Show Material materials with Temperatura de reblandecimiento Vicat of 174 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 76 mm/min |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 7 g/10min | ISO 1133 | 190°C/2.16kg |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm |