Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 1.1 % Show Material materials with Absorción de agua of 1.1 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.49 g/cm³ Show Material materials with Densidad of 1.49 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Dureza Rockwell M | 23.0 °C | 100 [-] Show Material materials with Dureza Rockwell M of 100 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 4.3 % Show Material materials with Elongación of 4.3 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 5.25 GPa Show Material materials with Módulo de flexión of 5.25 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5.5 GPa Show Material materials with Módulo elástico of 5.5 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 175 MPa Show Material materials with Resistencia a la flexión of 175 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 95 MPa Show Material materials with Resistencia a la tracción of 95 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU |
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 50 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 5 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 174 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 174 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 164 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 164 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 30mil | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 160 °C Show Material materials with Temperatura de reblandecimiento Vicat of 160 °C | ISO 306 | 90°F/h, 11 lbf | |||
Inflamabilidad | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 46 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.7 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.7 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+13 Ω·cm Show Material materials with Volume resistivity of 1.00E+13 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1 % Show Material materials with Contracción of 1 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | ISO 294-4, 2577 |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm | |