General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.9 % Show Material materials with Absorción de agua of 0.9 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Dureza Rockwell M | 23.0 °C | 93 [-] Show Material materials with Dureza Rockwell M of 93 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 27 % Show Material materials with Elongación of 27 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 13 % Show Material materials with Elongation at yield of 13 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 73.5 MPa Show Material materials with Límite elástico of 73.5 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 3.15 GPa Show Material materials with Módulo de flexión of 3.15 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.35 GPa Show Material materials with Módulo elástico of 3.35 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 8.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8.5 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 225 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 225 kJ/m² | ISO 179/1eU |
23.0 °C | 250 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 250 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 159 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 159 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 103 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 103 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 5E-4 [-] Show Material materials with Dissipation factor, 100Hz of 5E-4 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 5.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 5.5E-3 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 43 kV/mm Show Material materials with Rigidez dieléctrica of 43 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 2 % Show Material materials with Contracción of 2 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.8 % Show Material materials with Contracción transversal of 1.8 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 14 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 14 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm |