Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Elongación | 23.0 °C | 18 % Show Material materials with Elongación of 18 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 13 % Show Material materials with Elongation at yield of 13 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 67 MPa Show Material materials with Límite elástico of 67 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.9 GPa Show Material materials with Módulo de flexión of 2.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.2 GPa Show Material materials with Módulo elástico of 3.2 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 100 °C Show Material materials with Relative temperature index, electrical of 100 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm |