General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Dureza Rockwell M | 23.0 °C | 95 [-] Show Material materials with Dureza Rockwell M of 95 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 13 % Show Material materials with Elongation at yield of 13 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 77 MPa Show Material materials with Límite elástico of 77 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 3.2 GPa Show Material materials with Módulo de flexión of 3.2 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.4 GPa Show Material materials with Módulo elástico of 3.4 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 6.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6.5 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 235 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 235 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 165 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 165 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 115 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 115 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 110 °C Show Material materials with Relative temperature index, electrical of 110 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 90 °C Show Material materials with Relative temperature index, mechanical impact of 90 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 95 °C Show Material materials with Relative temperature index, mechanical strength of 95 °C | UL 746B | 120mil | |
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 30 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 100 Hz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 4E-3 [-] Show Material materials with Dissipation factor, 100Hz of 4E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 4.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 4.5E-3 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.8 % Show Material materials with Contracción of 1.8 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.8 % Show Material materials with Contracción transversal of 1.8 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 14 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 14 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Time, Dehumidified Dryer: 2-4h, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm |