General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.35 % Show Material materials with Absorción de agua of 0.35 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.53 g/cm³ Show Material materials with Densidad of 1.53 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.34 [-] Show Material materials with Coeficiente de Poisson of 0.34 [-] | |
Elongación | 23.0 °C | 2.5 % Show Material materials with Elongación of 2.5 % | ISO 527-1/-2 |
Módulo elástico | 23.0 °C | 9.9 GPa Show Material materials with Módulo elástico of 9.9 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 145 MPa Show Material materials with Resistencia a la tracción of 145 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 30 kJ/m² | ISO 179/1eU |
23.0 °C | 60 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 60 kJ/m² | ISO 179/1eU | |
Resistencia al cizallamiento | 23.0 °C | 75 MPa Show Material materials with Resistencia al cizallamiento of 75 MPa | ASTM D 732 |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 1730 J/(kg·K) Show Material materials with Calor específico of 1730 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 3E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 3E-5 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 223 °C Show Material materials with Temperatura de fusión of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, Oxygen index: 19 %, Glow Wire Flammability Index, 120mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.1 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.1 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 2.1E-3 [-] Show Material materials with Dissipation factor, 100Hz of 2.1E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 39 kV/mm Show Material materials with Rigidez dieléctrica of 39 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 375 V Show Material materials with Índice de seguimiento comparativo of 375 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.3 % Show Material materials with Contracción of 0.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.1 % Show Material materials with Contracción transversal of 1.1 % | ISO 294-4, 2577 |
Velocidad de flujo del volumen derretido | 19 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 19 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 240°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |