Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.9 % Show Material materials with Absorción de agua of 0.9 % | Sim. to ISO 62 | 80mil |
Coefficient of friction | 0.32 [-] Show Material materials with Coefficient of friction of 0.32 [-] | ASTM 1894 | 1h against itself | |
Densidad | 23.0 °C | 1.34 g/cm³ Show Material materials with Densidad of 1.34 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.43 [-] Show Material materials with Coeficiente de Poisson of 0.43 [-] | |||
Dureza Rockwell M | 23.0 °C | 58 [-] Show Material materials with Dureza Rockwell M of 58 [-] | ISO 2039-2 | ||
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | min. | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 30 % Show Material materials with Elongation at yield of 30 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 105 [-] Show Material materials with Hardness, Rockwell R of 105 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 1.1 GPa Show Material materials with Módulo de flexión of 1.1 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 1.4 GPa Show Material materials with Módulo elástico of 1.4 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 18 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 18 kJ/m² | ISO 179/1eA | ||
23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 90 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 20 kJ/m² | ISO 180/1A | ||
23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 90 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.3E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.4E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.4E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 100 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 100 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 170 °C Show Material materials with Temperatura de reblandecimiento Vicat of 170 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -35 °C Show Material materials with Temperatura de transición del vidrio of -35 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 550 °C, Glow Wire Flammability Index, 80mil: 550 °C, Glow Wire Flammability Index, 120mil: 550 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 41 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Constante dieléctrica, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.4 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.4 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.8 % Show Material materials with Contracción of 0.8 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.1 % Show Material materials with Contracción transversal of 1.1 % | ISO 294-4, 2577 |
Velocidad de flujo del volumen derretido | 1.7 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 1.7 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm | |
| Wear resistance | 60.0 | |