General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.37 g/cm³ Show Material materials with Densidad of 1.37 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Material materials with Coeficiente de Poisson of 0.4 [-] | |
Dureza Rockwell M | 23.0 °C | 69 [-] Show Material materials with Dureza Rockwell M of 69 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 29 % Show Material materials with Elongación of 29 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 20 % Show Material materials with Elongation at yield of 20 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 116 [-] Show Material materials with Hardness, Rockwell R of 116 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 54 MPa Show Material materials with Límite elástico of 54 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2 GPa Show Material materials with Módulo de flexión of 2 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 2 GPa Show Material materials with Módulo elástico of 2 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 136 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 136 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 78 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 78 °C | ISO 75-1/-2 | |||
Temperatura de reblandecimiento Vicat | 172 °C Show Material materials with Temperatura de reblandecimiento Vicat of 172 °C | ISO 306 | 90°F, 2 lbf | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Material materials with Contracción of 1.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.5 % Show Material materials with Contracción transversal of 1.5 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 6 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6 g/10min | ISO 1133 | 190°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm | |