General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.41 g/cm³ Show Material materials with Densidad of 1.41 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Dureza Rockwell M | 23.0 °C | 84 [-] Show Material materials with Dureza Rockwell M of 84 [-] | ISO 2039-2 |
Elongación | 23.0 °C | 40 % Show Material materials with Elongación of 40 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 21 % Show Material materials with Elongation at yield of 21 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Material materials with Hardness, Rockwell R of 117 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 66 MPa Show Material materials with Límite elástico of 66 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.9 GPa Show Material materials with Módulo de flexión of 2.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3 GPa Show Material materials with Módulo elástico of 3 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 8.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8.5 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 270 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 270 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 158 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 158 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 96 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 96 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 176 °C Show Material materials with Temperatura de fusión of 176 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Silicone Fluid |