General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.39 g/cm³ Show Material materials with Densidad of 1.39 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.39 [-] Show Material materials with Coeficiente de Poisson of 0.39 [-] | |
Elongación | 23.0 °C | 30 % Show Material materials with Elongación of 30 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 17 % Show Material materials with Elongation at yield of 17 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 55 MPa Show Material materials with Límite elástico of 55 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Material materials with Módulo de flexión of 2.1 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 2.3 GPa Show Material materials with Módulo elástico of 2.3 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 9 kJ/m² | ISO 180/1A |
-30.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 9 kJ/m² | ISO 180/1A | |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 12 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 55 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.5 % Show Material materials with Contracción of 1.5 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.6 % Show Material materials with Contracción transversal of 1.6 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 12 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 12 g/10min | ISO 1133 | 190°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |