General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.7 % Show Material materials with Absorción de agua of 1.7 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.23 g/cm³ Show Material materials with Densidad of 1.23 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.35 [-] Show Material materials with Coeficiente de Poisson of 0.35 [-] | |
Elongación | 23.0 °C | 2.7 % Show Material materials with Elongación of 2.7 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 4.9 GPa Show Material materials with Módulo de flexión of 4.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 5.5 GPa Show Material materials with Módulo elástico of 5.5 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 190 MPa Show Material materials with Resistencia a la flexión of 190 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 120 MPa Show Material materials with Resistencia a la tracción of 120 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.5 kJ/m² | ISO 180/1A |
23.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.5 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.6E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.5E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.5E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 258 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 238 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 238 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Temperatura de fusión | 262 °C Show Material materials with Temperatura de fusión of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 26 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 13% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |