General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.4 % Show Material materials with Absorción de agua of 0.4 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.06 g/cm³ Show Material materials with Densidad of 1.06 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.38 [-] Show Material materials with Coeficiente de Poisson of 0.38 [-] | |||
Elongación | 23.0 °C | 17 % Show Material materials with Elongación of 17 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 114 [-] Show Material materials with Hardness, Rockwell R of 114 [-] | ISO 2039-2 | ||
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 2.1 GPa Show Material materials with Módulo de flexión of 2.1 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Material materials with Módulo elástico of 2.4 GPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4.5 kJ/m² | ISO 180/1A | ||
23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2750 J/(kg·K) Show Material materials with Calor específico of 2750 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.6E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Temperatura de fusión | 218 °C Show Material materials with Temperatura de fusión of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 181 °C Show Material materials with Temperatura de reblandecimiento Vicat of 181 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 65 °C Show Material materials with Temperatura de transición del vidrio of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.85 mm, UL recognition: yes -, Oxygen index: 27 %, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: DNI - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 30 kV/mm Show Material materials with Rigidez dieléctrica of 30 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Material materials with Contracción of 1.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 35 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 35 g/10min | ISO 1133 | 230°C/1kg |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C |